Meie peamiselt HSS-puuriteratoodete jaoks on erinevad pretsessioonid, nagu valtsitud sepistamine, servade lihvimine ja freesimine.
Tutvustame neid tüüpe järgmiselt:
1.Roll Forged: the high speed steel is stretched and twisted according to a certain extent in the heating and softening and then roll forged the flute.
Näiteks: 70 mm üldpikkust saab venitada 100 mm-ni. Seega võib rull-sepistatud protsess materjale säästa ja selle maksumus on madal. Ja kaubad
Are very cheap.
2. Edge Ground: it is to fine finish the goods on the basis of roll forged and make the shank diameter more precious. So the goods are more easy to drill holes
Ja ka väljavaade paistab varasemast parem.
3.Milled: the high speed steel is milled the flute by the milling cutter. Because the material is not stretched or twisted, so the run-out of goods made by milled is more precise than the goods made by roll forged. At the same time, the milled process takes the semi-automatic machine, so it needs people to control the machine,
Ja see suurendab kulusid. Üldiselt kasutatakse freesimisprotsessi suurte puuriterade jaoks.
4. Täielikult jahvatatud on teine protsess puuriterade valmistamiseks. Nagu me teame, kasutatakse üldiselt jahvatatud protsessi
the large size(>13 mm)puuriteradest. Nii et tavalise suurusega (vähem kui 13 mm või sellega võrdne) puuriterade puhul kasutame täielikult jahvatatud protsessi.
The fully ground process takes the automatic machine. And the high speed steel is grinding the flute by the emery cutter.
Seega on see väga tõhus ja väga stabiilse kvaliteediga.